Hesse FABUMATT Excimer lacquer HUU 82000 clear

  • excimer convolution even for 3D workpieces
  • dull matt with 3.5 - 3.6 gloss (60°)
  • extremely scratch resistant
  • resistant against shiny areas
FABUMATT is a colourless top coat with outstanding resistance and an extremely matt gloss level. Its special formulation means this HYDRO-UV Top coat is suitable for three-dimensional workpieces. After convolution and complete hardening of the lacquer it produces extremely dull matt surfaces (3.5 - 3.8 gloss / 60°). Chemical resistance to DIN 68861-1A and scratch resistance of 1.3 N according to DIN 15086 (Method B) ensure that your workpieces have hard-wearing surfaces with an anti-fingerprint effect.
Request product Download data sheet
  • Description
  • Information on use
  • Sample process
  • Safety Data Sheets / Certificates

Fields of application

Used to produce high-quality and eco-compliant products in the furniture, door, kitchen and bathroom furniture industries. Particularly suitable for components with edges, profiles or milled sections in furniture fronts and interior doors. For use on systems with one excimer emitter and one UV emitter.

Technical specifications

Appearance colourless
Density series kg/l 1.071
Flow time (+/- 15 %) 30 s / DIN 53211 - 6 mm
Form of delivery fluid
Non-volatile content series % 45
VOC EU % 0.67 %
Number of coats (max) 1
Amount per layer (minimum) 80 g/m²
Amount per layer (max) 120 g/m²
Total application volume 120 g/m²

Information on use

Stackable after Directly after UV curing and sufficient cooling.
Curing A combination of different emitters will be required for complete hardening of the lacquer film. This includes the need to use an excimer emitter (wavelength 172 nm). The exact parameters will be agreed with you and captured in a "Guide to Finishing Techniques" (GFT).
Mechanical drying Array
Surface preparation The substrate must be dry, dust-free and grease-free.
Substrate sanding grits from-to 150 - 240
Lacquer sanding (grit) from - to 280 - 400
Finishing Coat with products from the same series after drying and lacquer sanding.
Comments on sanding Sanded lacquer layers and surfaces must be coated directly.
Yield per coat 9 - 13 m²/l

The spreading rate is heavily dependent on the type of application. The specifications relate to a liter of ready-for-use product, if necessary including hardener and thinner.
Working Temperature Range 15 - 35 °C
Storage temperature 10 - 35 °C
Working temperature 20 °C
conditions of transport frost-free - up to a maximum of 35 °C
Processing instructions Working viscosity can be adjusted with water or HYDRO Optimizer HZ 70 (maximum 3 % by volume). For strip cleaning, we recommend the HYDRO Cleaner HY 6995 at a mixing ratio of 1 : 10 with water. Remove dried-on lacquer residues with special thinner ZD 82.
Particular instructions Always seal opened containers light-tight and air-tight to prevent skin forming. Remove dried lacquer residue using a sieve. Products in containers should be sieved before application.
General instructions on workmanship When applying HYDRO materials, parts that come into contact with the material must be made from non-rusting material. The wood moisture content should be between 8 and 12 %. Stir the material well before application. Do not apply or dry HYDRO lacquers at material or room-temperatures below 18 °C. The ideal ambient humidity for application lies between 55 and 65 %. A humidity level that is too low leads to shrink cracks during the lacquering process; humidity that is too high hinders drying. Please freshly sand the lacquered surfaces before coating and apply lacquer to the sanded surfaces as soon as possible to prevent adhesion problems. When applied on laminates, etc., please use a sample coating on the respective substrate to check the adhesion! Final hardness of the coating is achieved after a week if stored at a minimum of 20 °C room temperature. Woods with rich contents, such as teak, may have an adverse effect on adhesion. Water-soluble ingredients in woods such as ash and tannins in woods such as oak may cause colour changes and discolorations in the coating. Always conduct a sample lacquering to evaluate the colour effect, adhesion and drying process under practical conditions.

The coating process and the precise treatment parameters are adapted in each case to the respective application and drying conditions and can be found in the customer-specific process descriptions (surface techniques).

Material Safety Data Sheets


Our technical information is continually adapted to keep up to date with the latest technology and statutory regulations. The latest version is always available online at www.hesse-lignal.de or talk to your local account manager. This information is for advice and is based on the best knowledge available and careful research in line with the current state of the art. This information cannot be held as legally binding. We also refer you to our terms and conditions of business. Safety data sheet is provided in accordance with EC regulation no. 1907/2006.